High Temperature Properties of AZ91D Magnesium Alloy Composite Reinforced with Short Alumina Fiber and Mg2Si Particle
Kazunori AsanoHiroyuki Yoneda
Author information

2008 Volume 49 Issue 7 Pages 1688-1693


Short alumina fiber- and in situ Mg2Si particle reinforced magnesium alloy composites were fabricated by squeeze casting. The in situ Mg2Si particles were formed during the infiltration with the melt into the preforms consisting of the fibers having Si particles attached to their surfaces. The microstructure of the composites and their tensile strength and Young’s modulus in the range from 293 K to 523 K were investigated. The effect of the Mg2Si particles on the tensile properties was examined by comparison with the properties of the fiber-reinforced composite without the Mg2Si particles. Fine Mg2Si particles with a grain size of approximately 5 μm were formed due to the rapid solidification in the permanent mold. The dispersion of the Mg2Si having a high Young’s modulus was found to be effective for improving Young’s modulus of the fiber-reinforced magnesium alloy composite. The experimental value of the composite was in good agreement with the calculated value based on a previously proposed model. The tensile strength of the composite with 18 vol% fibers and Mg2Si particles was higher than that of the conventional fiber-reinforced composite at both room temperature and high temperature. Examination of the fracture surfaces indicated that stress transmission between the fiber and the matrix became easy due to the particles, which reduced the fiber-to-fiber contact.

Information related to the author
© 2008 The Japan Institute of Metals and Materials
Previous article Next article