2013 Volume 54 Issue 2 Pages 184-187
The ordered–disordered phase transformation temperature and time of Cu–Zn alloy before and after 2 GPa pressure treatment were measured by differential scanning calorimeter (DSC). The phase transformation activation energy and Avrami exponent were calculated and the effect of 2 GPa pressure treatment on the microstructure evolution was also discussed based on the kinetic parameters. The results show that 2 GPa pressure treatment on Cu–Zn alloy from ordered (β′) to disordered (β) phase transformation shift to the low temperature region and can shortened the phase transformation time in the subsequent heating process, which is helpful to the formation of the microstructure with a fine grain size in Cu–Zn alloy, but no new phase is generated.