Kinetics of Solid-State Reactive Diffusion between Co and Sn
Minho OYoshiki TakamatsuMasanori Kajihara
Author information
JOURNALS FREE ACCESS

2014 Volume 55 Issue 7 Pages 1058-1064

Details
Abstract

To examine growth behavior of α-CoSn3 at solid-state temperatures, kinetics of reactive diffusion between Co and Sn was experimentally observed using sandwich Sn/Co/Sn diffusion couples prepared by a diffusion bonding technique. The diffusion couples were isothermally annealed in the temperature range of 433–473 K for various times up to 744 h. Owing to annealing, an intermetallic layer consisting of CoSn3 was formed at the original interface in the diffusion couple. The mean thickness of the intermetallic layer increases in proportion to a power function of the annealing time. The exponent of the power function takes values of 0.67 and 0.62 at 433–453 and 473 K, respectively. These values of the exponent indicate that volume diffusion predominantly controls the layer growth and interface reaction partially contributes to the rate-controlling process.

Information related to the author
© 2014 The Japan Institute of Metals and Materials
Previous article Next article
feedback
Top