Prediction of In-Plane Anisotropy of Bendability Based on Orientation Distribution Function for Polycrystalline Face-Centered Cubic Metal Sheets with Various Textures
Hirofumi Inoue
Author information
JOURNALS FREE ACCESS

2015 Volume 56 Issue 1 Pages 61-69

Details
Abstract

Bendability of sheet metals is strongly affected by crystallographic orientation and it has recently been found that the bendability has a correlation with the Taylor factor in Al-Mg-Si and Cu-Ni-Si alloy sheets. This paper has proposed an analytical method for predicting in-plane anisotropy of bendability in polycrystalline face-centered cubic metal sheets by using the mean value of Taylor factors for all grains calculated from an orientation distribution function. The calculation was performed on the assumption that a strain condition at the convex surface during bending deformation is close to plane strain tension. Using various ideal orientations with Gaussian distribution and various real textures of annealed aluminum or copper alloys, the normalized Taylor factor, which was defined as a ratio of the mean Taylor factor for a textured material to that for a randomly oriented one, was compared with some known experimental data on bendability at directions of 0° and 90° to the rolling direction. The results clearly showed that bendability was better at the bending direction with a lower normalized Taylor factor. Since the formation of shear bands at the sheet surface causes deterioration of bendability, the present analytical method based on the normalized Taylor factor will have the advantage of giving us a prediction of bendability at arbitrary directions in a sheet, if textures of metal sheets are measured on the surface without polishing by means of X-ray diffraction.

Information related to the author
© 2014 The Japan Institute of Metals and Materials
Previous article Next article
feedback
Top