2015 Volume 56 Issue 8 Pages 1307-1309
New observations of time dependent magnetization of an Al-1.6%Mg2Si alloy over a range of constant temperatures between 250 K and 310 K are presented. The post solution heat treatment time variations of magnetization at 300 and 310 K increased with time out to about 1300 minutes, whereas those at 280 and 290 K showed minima around 150 and 50 minutes, respectively. The magnetization at 250 K initially decreased slightly and then became constant with time. The observed time variations of magnetization are explained in terms of clustering reactions of the Mg, Si and vacancies.