Aging Behavior of In-Situ TiB2 Particles Reinforced 2014Al Alloy Composites
Jing XueLuling ZhangJun WangRenjie Wan
Author information
JOURNALS FREE ACCESS FULL-TEXT HTML

2017 Volume 58 Issue 1 Pages 33-38

Details
Abstract

In-situ TiB2 particles reinforced 2014Al alloy matrix composite was prepared using an exothermic reaction process with K2TiF6 and KBF4 salts. The age-hardening behaviors of in-situ TiB2/2014Al composites were studied using Vickers-hardness measurement, DSC and TEM. The results indicated that TiB2 particles had a considerable effect on the aging response of 2014Al alloy matrix in the composite. Due to the introduction of TiB2 particles, the time to achieve peak hardness in the composite is shorter at three aging temperatures compared with that of 2014Al alloy. While the age-hardness efficiency of the composites was lower than that of 2014Al alloy. Formation of G.P. zones was suppressed in composite, which was believed to be due to the introduction of vast particle-matrix interfaces that acted as a sink for vacancies during quenching. Moreover, TiB2 particles caused increase in thermal-diffusion activation energy of θ′ phase during aging, which made the precipitation of θ′ phase more difficult. And the number and size of precipitates in the composite were relatively less and smaller than that of 2014Al alloy.

Information related to the author
© 2016 The Japan Institute of Metals and Materials
Previous article Next article
feedback
Top