2025 Volume 66 Issue 10 Pages 1287-1296
In this study, Ti-Zr-Sc sintered alloys with excellent biocompatibility were fabricated from the elemental mixture of pure Ti, ZrH2 and ScH2 powders, and their microstructures and mechanical properties were investigated to clarify the strengthening mechanism. In particular, the effect of scandium (Sc) used as the third alloying element on the strengthening behavior by grain refinement, oxygen (O) and Sc solid solution, and Sc2O3 particle dispersion was quantitatively evaluated by using the theoretical strengthening models. 0.2% YS of Ti-Zr-Sc alloys decreased with Sc content in the range of 0∼1.0 at.% Sc, and increased in the range of 1.0∼2.5 at.% Sc. In the former, the added Sc elements reacted with O solutes to form Sc2O3 particles and resulted in a significant decrease of O solid solution strengthening effect. On the other hand, when Sc content was over 1.0 at.%, the strengthening effects by both Sc solid solution and Sc2O3 dispersion were effective, and cause a remarkable increment of 0.2% YS of Ti-Zr-Sc sintered alloys.
This Paper was Originally Published in Japanese in J. Jpn. Soc. Powder Powder Metallurgy 71 (2024) 482–491, https://doi.org/10.2497/jjspm.23-00067. The citation in reference 35 is corrected.