抄録
Edge dislocations in wurtzite-type CdSe single crystals were observed by etching technique, and etch pit densities were measured along its low-angle grain boundaries, and also for crystals which were bent around the caxis at 250_??_500°C. The results indicate a good correspondence between the edge dislocations and etch pits.