抄録
Understanding and controlling solidification and phase transformation process of weld metal is essential for forming the microstructure with superior mechanical property. Recent evolution of analysis technique makes for solidification and phase transformation process to be in-situ analyzed, in direct and reciprocal lattice space.
In the present work, unidirectional-solidification and phase transformation in the weld metal of commercial pure-titanium in Gas Tungsten Arc welding was in-situ observed by using Time-Resolved X-Ray Diffraction system with two-dimensional pixel detector. An undulator beam was used as a probe. Larger diffraction area could be detected in the time-resolution of 0.05 seconds, in unidirectional solidification and subsequent phase transformation process of pure-titanium weld metal. Furthermore, the microstructure formation during β-α phase transformation was in situ observed with High temperature Laser Scanning Confocal Microscopy.
The crystal configurations in unidirectional solidification of weld metal and rapid change of phase ratio in reconstructive phase transformation were clearly analyzed.