接合組立型cBN・フリット/Al2O3・フリット製研削砥石の開発
深谷 保博末田 穣松本 隆博塚本 頴彦江川 庸夫広実 常登吉岡 肇濱本 徳也
著者情報
ジャーナル フリー

1993 年 11 巻 4 号 p. 503-509

詳細
抄録

Research and development of grinding wheel bonded cBN·frfrit/Al2O3·frit (laped sintering) to outer surface of metal ring were conducted. Ag-Cu-Ti brazing was applied for bonding method in stead of conventional adhesive agent method.
Main results obtAlned are as follows.
(1) The relief of residual thermal stress and operating stress at joint are important. It was concluded by calculation of stress that use of Kovar for metal ring was effective for thermal stress relief at bonding and slit cutting to Kovar ring was effective for operating stress relief at rotating.
(2) New grinding wheel fabricated with the above mentioned procedure rotated by peripheral speed 290 m/s at spin test. From this spin test result, it was confirmed that this wheel had excellent rotating characteristic compared with conventional wheel (adhesive agent method).

著者関連情報
© 一般社団法人 溶接学会
前の記事 次の記事
feedback
Top