2014 Volume 51 Issue 3 Pages 163-168
Plate-like Ti3SiC2 particles were prepared. Highly textured and dense Ti3SiC2 ceramics was successfully fabricated by slip casting plate-like particles in a strong magnetic field followed by pulsed electric current sintering at 1450℃under 80 MPa for 5min. 3 point bending strength and K1C of the textured Ti3SiC2 ceramics were 812 MPa, 7.3 MPa・m1/2, respectively. Compared to the Ti3SiC2 ceramics prepared by slip casting without magnetic field, the 3 point bending strength and K1C of the textured Ti3SiC2 ceramics have been increased by factors of 1.05 and 1.22, respectively.