高炉融着帯・滴下帯領域での溶融酸化鉄によるコークスの劣化

抄録

In order to clarify degradation of coke in the cohesive zone and the dripping zone of a blast furnace, the fundamental experiment about coke degradation reacted to molten FeO was carried out. The difference of coke degradation reacted to molten FeO and CO₂ gas is discussed. The results are as follows.
(1) Coke reacted to molten FeO forms dimple and thin reacted layer locally. Coke reacted to CO₂ gas forms thick reacted layer around lumpy coke.
(2) Coke reacted to CO₂ gas discharges more fine coke than coke reacted to molten FeO. Coke reacted to molten FeO discharges particles.
(3) Fine ratio of coke reacted to molten FeO is suppressed with increasing coke strength.