鋼中微量酸素定量における前処理法の影響

抄録

Removing the oxide film from the sample surface is an important process for analyzing trace oxygen in iron and steel.
The depth profiles of oxygen on the surface after electro-polishing in CH₃COOH-HClO₄, CrO₃-H₃PO₄, and chemical polishing by HF-_H2O₂ were investigated.
As for the high-purity iron, thickness of the oxide layer after electro-polishing in CrO₃-H₃PO₄was thicker than any other pretreatment methods. This is because Fe(III) hydroxide was formed on the surface of sample. This could be removed by rinsing with an acid after electropolishing.
As for the bearing steel, oxygen containing species were found around carbides on the surface of the sample after pretreatment except that the pretreatment was made by electro-polishing in CrO₃-H₃PO₄. Those precipitates influenced the analysis of oxygen.
Analytical value obtained by conventional methods were 1 or 2 mass ppm higher than those obtained by charged particle activation analysis that is not influenced by surface contamination. This difference corresponds to the oxide layer formed on the sample surface.