応力分布Tスケーリング法適用による圧縮残留応力付与時破壊靭性値の予測
石原 健一下池 利孝飯井 俊行
著者情報
ジャーナル フリー

2017 年 83 巻 855 号 p. 17-00323

詳細
抄録

The fracture toughness Jc of the material in the ductile to brittle transition temperature (DBTT) region shows test specimen thickness (TST) effect and temperature dependence, and apparently increases when compressive residual stress is applied. In this paper, as TST effect and temperature dependence, the fact that Jc apparently increases due to compressive residual stress is attributable to the loss in the one-to-one correspondence between J and the crack-tip stress distribution, and then, the fracture prediction of the specimen with compressive residual stress was performed using the T-scaling method proposed by the authors, and its validity was confirmed for high strength steel of 780 MPa class and 0.45 % carbon steel JIS S45C. In addition, it was suggested that the minimum of Jc with compressive residual stress can be predicted by requiring only the tensile test.

著者関連情報
© 2017 一般社団法人日本機械学会
前の記事 次の記事
feedback
Top