オーステナイト系ステンレス鋼のSSRT特性に及ぼす外部・内部水素の影響と加工誘起マルテンサイト変態の役割
松岡 三郎古谷 佳之竹内 悦男蛭川 寿松永 久生
著者情報
ジャーナル フリー 早期公開

論文ID: 20-00306

この記事には本公開記事があります。
詳細
抄録

In order to investigate the effect of hydrogen on Slow Strain Rate Tensile (SSRT) test of austenitic stainless steels, SUS304, SUS316 and SUS316L, two types of SSRT tests were conducted. One is the external hydrogen SSRT test that was conducted in hydrogen gas at temperatures of T = −40 ~ 200℃ and pressures of p = 87 ~ 115 MPa using non-charged specimen. Another is the internal hydrogen SSRT test that was conducted in ambient air or 0.1 MPa nitrogen gas at T = −120 ~ 200°C using hydrogen-charged specimen exposed to hydrogen gas at p = 68 or 100 MPa. SSRT properties (i.e., relative reduction in area, RRA, and relative tensile strength, RTS) obtained in the external and internal hydrogen tests corresponded to each other. The results inferred that the internal hydrogen test can be a substitute for the external hydrogen test. Furthermore, the temperature dependence of RRA and RTS was evaluated based on the austenite stability of materials, which was represented by Md30 temperature, in association with martensitic transformation-induced plasticity. It was found that RRA and RTS of SUS304, SUS316 and SUS316L having different austenitic stabilities were successfully unified by using the novel parameter, TMd30.

著者関連情報
© 2020 一般社団法人日本機械学会
feedback
Top