1981 年 30 巻 10 号 p. 678-679
Fabrication of a solid membrane type sodium ionselective electrode based on ion-implanted alumina wafer and its characteristics are described. Alumina wafer had the thickness of 100μm and the diameter of 1.40 cm. Ion-selective membrane, was fabricated that Li+, Si+ was implanted on the both side of single crystal alumina wafer. The total dose of Li+, Si+ was the same, viz., 1014/cm2. The response curve had the slope of 42 mV/pNa in the concentration range (10010-4) mol/l. The full response was achieved after ca. 1 min, and the response was reproducible.