抄録
Hydrophobically modified hydroxypropyl methylcellulose (HM-HPMC), a polymer in which a small amount of HPMC is stearoxyl substituted, was used as an emulsifier of emulsion-type lotion. A high-pressure homogenizer (microfluidizer) was used. The viscosity of the 1% HM-HPMC aqueous gel decreased after passing through the microfluidizer from 5.5 to 2.7 Pa·s. When liquid paraffin (LP) was used as the oil phase, a stable emulsion was obtained with an LP ratio of 1–40%. The apparent viscosity decreased with LP ratios up to 20%, and then increased with increasing LP concentration. The emulsions with an LP ratio <20% presented a pseudo-viscous flow, similar to that of the diluted polymer solution. HM-HPMC likely adsorbed onto the oil with a stearoxyl group; thus, the interaction between the stearoxyl group, which explained the high viscosity of HM-HPMC, decreased, reducing the viscosity of the emulsion. The LP ratio was 40%, and the emulsion presented a plastic flow, which is typical of concentrated emulsions. The size of the droplet in the emulsion was approximately 1 µm regardless of the LP ratio. When low-viscosity LPs or monoester-type oils such as isopropyl myristate were used, some of the emulsions presented creaming. An emulsion using HM-HPMC as an emulsifier and an appropriate oil homogenized with a microfluidizer is stable, has low viscosity, and can be easily spread on skin.