2007 Volume 26 Issue 4 Pages 568-574
To reduce the leachability of reducing agents from composite resins, immobilization of a simulated reducing agent at the surface of SiO2 fillers was examined. SiO2 plates were immersed in 2% 3-aminopropyltriethoxy silane/ethanol solution, and then immersed in dimethyl sulfoxide with 0.25 wt% 4-dimethyl amino benzoic acid (DMABA), 2.0 wt% 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide hydrochloride, and 0.5 wt% N-hydroxysuccinimide. Wide-scan spectrum of X-ray photoelectron spectroscopy did not detect carbon contamination. However, narrow scan detected an O=C-N peak at 399.8 eV, suggesting that DMABA could be immobilized on silane-coupled SiO2 plates. Further, surface plasmon resonance analysis indicated the adsorption of MMA at the surface of reducing agent-immobilized plate.