Study on fabrication of orthodontic brackets with the photocatalytic function of titanium dioxide
Yosuke SATOKen MIYAZAWANatsu SATOKenjiro NAKANOYukiko TAKEITatsushi KAWAIShigemi GOTO
Author information
JOURNAL FREE ACCESS

2009 Volume 28 Issue 4 Pages 388-395

Details
Abstract
We sought to investigate whether the photocatalytic function of rutile-type titanium dioxide is applicable for orthodontic brackets. To this end, TiO2 specimens were compressed and sintered. Then, each specimen was analyzed by X-ray diffraction to confirm that no compositional changes had taken place. Next, the surface of each specimen was observed with a colorimeter, scanning electron microscope (SEM), and atomic force microscope (AFM). Fundamental material properties after calcination were measured. The photocatalytic function was evaluated using the decolorization method with toluidine blue. The following were observed with the increase of calcinations temperature: growth of crystal particles, decrease in surface roughness and surface brightness, but increase in shrinkage percentage and compressive strength. The aesthetic and mechanical properties of TiO2 material were adequate when compared with other bracket materials. In addition, it had a satisfactory photocatalytic function after high-temperature calcination. Based on the favorable results obtained, rutile-type titanium dioxide seemed to be applicable for the fabrication of self-cleaning orthodontic brackets.
Content from these authors
© 2009 The Japanese Society for Dental Materials and Devices
Previous article Next article
feedback
Top