抄録
We compared the surface free energies and enamel bond strengths of single-step self-etch adhesives with and without an oxygen-inhibited layer. The adhesives were applied to the enamel surfaces of bovine incisors, light irradiated, and the oxygen-inhibited layer was either retained or removed with ethanol. The surface free energies and their components (γSLW, γS+, and γS−) were determined by measuring the contact angles of three test liquids placed on the cured adhesives. The enamel bond strengths of specimens with and without the oxygen-inhibited layer were measured. For all surfaces, the value of the estimated surface tension component γSLW was relatively constant. The value of the γS+ component increased slightly when the oxygen-inhibited layer was removed, whereas that of the γS− component decreased significantly. The enamel bond strengths of the self-etch adhesives were significantly lower in the specimens without an oxygen-inhibited layer. The oxygen-inhibited layer therefore appeared to promote higher enamel bond strength.