The aim of this study was to investigate coronal leakage after obturation with mineral trioxide aggregate (MTA), resin-based sealer, and silicon-based sealer for open apical foramina and to evaluate pathway of leakage. Twenty-eight maxillary premolars were used, and instrumented to ISO size #80. Teeth were randomly divided into four groups as follows: Group A filled with MTA, Group B with gutta-percha and resin-based sealer, Group C with polymer-based material and resin-based sealer, and Group D with gutta-percha and silicon-based sealer. All samples were evaluated for coronal leakage with methylene blue solution and spectrophotometry. After leakage testing, samples were cut, and sections were observed. Dye leakage of Group A was significantly lowest among all groups at 15 days and 30 days. Defects which induced coronal leakage in resin-based sealer were observed at 7 mm from the apex. Coronal leakage after obturation with MTA for open apical foramina was significantly lower than resin-based sealer and silicon-based sealer.