Effects of the addition of fluoride to a 4-META/MMA-TBB-based resin adhesive on fluoride release, acid resistance of enamel and shear bond strength in vitro

抄録

This study investigated fluoride release, acid resistance and shear bond strength (SBS) of new 4-META/MMA-TBB-based fluoridecontaining resin adhesive (Super-Bond/F3). Super-Bond, Transbond Plus and Fuji Ortho LC were selected for comparison. Fluoride release into distilled water during 6-month period was measured using disk-shaped specimens. Brackets were bonded to human premolars with each material and then the specimens for the nanoindentation test were subjected to alternating immersion (demineralizing and remineralizing solutions); the hardness and elastic modulus of the enamel around bracket were determined. Rest of the specimens was subjected to examine the SBS. Super-Bond/F3 and Fuji Ortho LC showed significantly greater fluoride release compared with the other materials. The reductions in hardness and the elastic modulus for Super-Bond/F3 and Fuji Ortho LC were lower than those for the other materilas. Super-Bond and Super-Bond/F3 showed significantly greater SBS than Fuji Ortho FC. In conclusion, Super-Bond/F3 showed high fluoride-release, cariostatic potential and equivalent SBS.