The purpose of this study was to evaluate how the temperature affects the stability of polymerized additional photoinitiator-containing composite resins. Five resin products were light-cured using a quartz-tungsten-halogen, and single and dual emission peaks lightemitting diodes. The degree of conversion (DC) and water sorption, solubility, and color change of the specimens were evaluated after immersion in the solutions of different temperatures (4, 37, and 60ºC) for 14 days. On the top surface, the light-curing units had no significant influence on DC of the tested specimens. On the bottom surface, the influence was inconsistent. As the solution temperature increased, water sorption also consistently increased in all specimens, whereas solubility changed inconsistently. Water sorption and solubility had a high linear correlation only at low temperature solution. Color change of the specimens was similar, mostly slight, and statistically inconsistent regardless of solution temperature. The restored composite resins are needed to avoid contact with hot solutions for durable dental restoration.