Chemical alteration of Ag-Pd-Cu-Au alloy surface by alumina air-abrasion and its effect on bonding to resin cement

Abstract

The goal of this study was to investigate the chemical alteration of a dental alloy surface by alumina air-abrasion and its effect on bonding to resin cement. Alumina air-abrasion was carried out on an Ag-Pd-Cu-Au alloy. The surface morphology and chemical state of the abraded alloy were characterized. The effect of the air-abrasion on the shear bond strength between the alloy and a methyl methacrylate/tri-n-butyl borane (MMA/TBB) resin cement with some primers was evaluated. The surface characterization revealed that the alumina air-abrasion mechanically roughened and chemically altered the surface. The chemical alterations had two effects: (1) abraded alumina particles remained on the alloy surface and (2) copper ions were oxidized in the alloy surface. As the result, the shear bond strength test indicated that 10-methacryloyloxydecyl dihydrogen phosphate (MDP) contained primer worked with the abraded alloy surface, whereas it did not work with the non-abraded alloy surface.