Effect of microslit retention on the bond strength of zirconia to dental materials

Abstract

The aim of this study was to investigate the effect of microslits formed by Nd:YVO₄ laser beam machining on the bond strength between two types of zirconia, yttria-partially stabilized zirconia (Y-TZP) and ceria-partially stabilized zirconia/alumina nanocomposite (Ce-TZP/A), and porcelain or two types of resin. Zirconia disks were divided into three groups: 1) non-treated (NT); 2) blasted with alumina particles (AB); 3) microslits fabricated on a zirconia surface by laser beam machining (MS). After veneering porcelain or resins on zirconia specimens, halves of the resin specimens were thermocycled up to 20,000 cycles. The shear bond strength between porcelain and both types of zirconia was not improved by the microslits. Before and after thermocycling, the bond strength between an indirect composite resin or acrylic resin and Y-TZP with microslits was the highest. It was concluded that the microslits on Y-TZP enabled micromechanical interlocking and improved the bond strength and durability of the resins.