Effects of different silica-based layer coatings on bond strength of Y-TZP to bovine dentin

Abstract

This study investigated the effects of different silica-based layer coatings on shear bond strength (SBS) between Y-TZP and bovine dentin. Three different silica-based layer coatings were applied to the Y-TZP surface: tribochemical silica coating, vitrification (glaze coating), and composite resin sintering. A silane coupling agent (SIL) was applied to the silica-coated Y-TZP surface in the presence or absence of hydrofluoric acid (HF) treatment. A one-step adhesive was then applied to the silica-coated Y-TZP and cemented to bovine dentin using MDP-free resin cement. The SBS value of the tribochemical silica coating group was lowest among the experimental groups, while the HF+SIL subgroup showed the highest SBS value after vitrification (p<0.05). While hydrofluoric acid etching did not affect the SBS value of the tribochemical silica coating group, it affected the SBS value in the vitrification and composite resin sintering groups (p<0.05).