2021 Volume 40 Issue 3 Pages 758-765
The purpose of this study was to characterize a chlorhexidine-encapsulated nanotube modified pit-and-fissure sealant for biofilm development prevention. HS (commercial control); HNT (HS+15wt%Halloysite®-clay-nanotube); CHX10% (HS+15wt% HNT-encapsulated with chlorhexidine 10%); and CHX20% (HS+15wt% HNT-encapsulated with CHX20%) were tested. Degree-of-conversion (DC%), Knoop hardness (KHN), and viscosity were analyzed. The ability of the sealant to wet the fissures was evaluated. Specimens were tested for zones of inhibition of microbial growth. S. mutans biofilm was tested by measuring recovered viability. Data were statistically analyzed (p<0.05). DC% was significantly higher for the HNT-CHX groups. For KHN, CHX10% presented a lower mean value than the other groups. Adding HNT resulted in higher viscosity values. The biofilm on CHX10% and CHX20% sealants presented remarkable CFU/mL reduction in comparison to the HS. The experimental material was able to reduce the biofilm development in S. mutans biofilm without compromising the sealant properties.