Dislodgement pushout resistance of five bioceramic root-end filling materials

抄録

This study evaluated the dislodgement push-out resistance of five bioceramic materials. One hundred single-rooted teeth with one canal had the apical 3 mm and crown resected to create a 14 mm standardized length. The canals were instrumented to an apical size 80 with a 3 mm root-end preparation made with ultrasonic diamonds. The prepared roots were randomly divided into 5 root-end restorative groups (n=20). ProRoot MTA, Biodentine, EndoSequence Root Repair Material, EndoSequence Fast Set Putty, and EndoSequence BC Sealer with each material placed following manufacturer’s instructions and stored at 100% humidity for 2 weeks. An apical-to-coronal static testing load with the identified dislodgement force converted into MPa with mean results analyzed with Kruskal-Wallis and Dunn’s post hoc tests (α=0.05). ProRoot MTA and Biodentine displayed similar push-out stress resistance and exhibited significantly greater stress resistance than the similar Endosequence materials. However, all materials failed cohesively and were not dislodged from the root canal surface.