論文ID: 2017-183
This study aimed to investigate how different compositions of experimental silane-based primers in a methyl methacrylate solution containing 3-(trimethoxysilyl)propyl methacrylate (3-TMSPMA) or 3-(4-methacryloyloxyphenyl)propyl trimethoxysilane (3-MPPTS) might act as silicon dioxide bonding agents. With or without post-silanization heat treatment, primer-treated quartz discs were bonded using the MMA-TBB resin and their bond strengths were evaluated. The disks were primed with one of the following materials: 1 mol% 3-TMSPMA, 2 mol% 3-TMSPMA, 1 mol% 3-MPPTS, and 2 mol% 3-MPPTS. Shear bond strength was determined both before and after thermocycling. Statistical analyses were performed with non-parametric procedure (Kruskal-Wallis, Mann-Whitney U, and Steel-Dwass tests). Both primers were effective with heat treatment to enhance bonding between quartz and the MMA-TBB, and the bonding durability of the 1 and 2 mol% 3-MPPTS (16.8 and 24.9 MPa) with heat groups was significantly higher than in the 1 and 2 mol% 3-TMSPMA (5.4 and 9.8 MPa) with heat groups.