Article ID: 2018-280
The purpose of the study was to test new method for in vitro evaluation of dental material wear with 3D digitization procedure. Thirty dental crowns, made of polyetheretherketone and veneered with composite material, were subjected to wear test. The crown surface was digitized using coordinate measuring machine before and after the performed wear test. Mesh 3D models were reconstructed and average and maximum depth of lost material and volume loss was calculated (GOM Inspect 2016 software). Mean average depth value amounted 12±7 µm, maximum depth value was 42 µm, while mean volume loss was 0.0024 mm3. The smallest measured values were 4 µm for depth value and 0.0003 mm3 for volume loss. Coefficient of variation was very high for all tested parameters (>50%) as a result of data inconsistency. Within the limitations of applied methodology, the possibility of using coordinate measuring machine in measurement of dental material wear was confirmed.