Preparation and properties of tristrontium aluminate as an alternative component of mineral trioxide aggregate (MTA) cement

Abstract

This study evaluated tristrontium aluminate (S₃A) and its viability as a component for tricalcium silicate (C₃S) cements. The properties of S₃A, C₃S, and S₃A/C₃S mixtures were evaluated in terms of setting time, compressive strength, flowability, and radiopacity. X-ray diffraction (XRD) pattern verified the powder synthesized in the laboratory as S₃A, consequently, confirming the preparation method. S₃A exhibited the lowest setting time, followed by C₃S and S₃A/C₃S mixtures. Compressive strength of C₃S was significantly higher than S₃A. The S₃A/C₃S mixture showed comparable compressive strength to C₃S for 1-day post initial mixing. There was no significant difference in flowability between S₃A/C₃S and mineral trioxide aggregate (MTA). S₃A showed comparable radiopacity to MTA, whereas that of the S₃A/C₃S mixture was significantly lower comparatively; however, it achieved sufficient radiopacity (3 mm aluminum thickness equivalent). Further studies are needed to improve the manufacturing process of S₃A and evaluate the bioactive effect of strontium.