Effect of supporting dies’ mechanical properties on fracture behavior of monolithic zirconia molar crowns
Yutao JIANTianyi ZHANGXiaodong WANGLaina KYAWEdmond Ho Nang POWKe ZHAO
著者情報
ジャーナル フリー 早期公開

論文ID: 2021-090

この記事には本公開記事があります。
詳細
抄録

The aim of this study was to investigate the effects of supporting dies with different mechanical properties on the fracture strengths and failure modes of monolithic zirconia crowns, and identify a suitable die material for testing high-strength ceramic restorations. Thirty six dies from teeth, porous titanium and composite-resin with 36 zirconia crowns were fabricated based on 3D model. Crowns were cemented, then underwent load-to-fracture testing. Fractographic analysis was performed with scanning electron microscopy, and finite element analysis was made. During loading, a high stress concentration zone formed near the loading point and on surface of die. Cracks generated on failure penetrated the crown and extended to die in 9 teeth group specimens, while composite-resin samples exhibited fracture of both crowns and dies. All dies remained intact in porous titanium group. Fracture mode was undistinguishable in all groups. It was concluded that porous titanium appears suitable as die material for dental restorations with high fracture strength.

著者関連情報
© 2022 The Japanese Society for Dental Materials and Devices
feedback
Top