Fracture strength of implant-supported hybrid abutment crowns in premolar region fabricated using different restorative CAD/CAM materials

抄録

The present study investigated the fracture strength of hybrid abutment crowns (HACs) in the premolar region that were fabricated with different restorative computer-aided design/computer-aided manufacturing (CAD/CAM) materials. The abutment-implant structures were randomly assigned into four groups (n=11 per group): bi-layered zirconia restorations (BL), translucent zirconia (4Y-PSZ) restorations (TZ), lithium disilicate ceramic restorations (LD), and dispersed nanoparticle-filled composite resin restorations (CM). All restorations were adhesively bonded to the titanium abutments. After the restoration-abutment complex was tightened onto the implant, the fracture strength was measured. The TZ (2.06 kN) and LD (1.87 kN) groups had significantly higher median fracture strengths than the BL (1.12 kN) and CM (1.10 kN) groups. In terms of fracture resistance, the 4Y-PSZ and lithium disilicate ceramic monolithic restorations would be superior to bi-layered 3Y-TZP and composite resin monolithic restorations for HACs in the premolar region.