論文ID: 2022-243
This review describes the development of ultra-high translucent zirconia (referred to as UHTZ) using new manufacturing technology and its characterization results. The development of UHTZ was primarily due to the adoption of two basic manufacturing technologies, “Cyclic CIP” and “Plus Y Technology”. This manufacturing technology could provide stable processing characteristics, which improves chipping resistance during milling. Furthermore, the enlargement factor (processing coefficient) for UHTZ is smaller than those for conventional products. In general, the higher the light transmittance, the lower the flexural strength. Despite its extremely high translucency, the most significant feature of UTHZ is that its flexural strength is comparable to that of 5Y. Furthermore, UHTZ has higher chemical durability and uniform microstructure, which results in less wear on the opposing teeth and superior discoloration resistance. Therefore, UHTZ is a new option for inlay, onlay, and laminate veneer applications, where lithium disilicate glass ceramics has been widely used.