This study investigated the effect of 10-methacryloyloxydecyl dihydrogen phosphate (MDP) in methyl methacrylate (MMA) monomer on the adhesion of tri-n-butylborane (TBB)-initiated resins (MDP/MMA-TBB resins) to human enamel. Enamel surface conditions were either polished only or phosphatized surfaces. The 1.0, 1.7, and 2.0 mol% MDP/MMA-TBB resins, 4-methacryloxyethyl trimellitate anhydride (4-META)/MMA-TBB resin and MMA-TBB resin were prepared as luting materials. The shear bond strength was determined before and after thermocycles, and the results were compared using non-parametric statistical analyses (each, n=15). The MDP/MMA-TBB resins showed significantly better bond durability to enamel than other resins with or without etching. The 1.7 and 2.0 mol% MDP/MMA-TBB resins were suggested to be the optimum MDP concentrations from pre- and post-thermocycling results for the non-etched specimens. The TBB initiator resin including MDP was shown to be effective in bonding to human enamel, and this effect was enhanced in combination with phosphate treatment.