2010 年 78 巻 5 号 p. 353-356
Lithium-air batteries using Ketjen Black-EC600JD for their air electrodes exhibited a rather large discharge capacity of about 3000 mAh g−1 at a current density of 0.05 mA cm−2. However, the cycle performance of the batteries was very poor due to the high overpotential for charging. The cycle properties were greatly improved by adding the Fe–Mn-based perovskite-type oxide, La0.6Sr0.4Fe0.6Mn0.4O3, to the air electrodes as an electrocatalyst.