抄録
“Habutae” fabric and silk bolting cloth were treated with organic silicon resin and the 1) amount of resin adhered 2) transmission degree of humidity 3) air permeability 4) water-proof 5) crease recovery were ascertained with the following results:
1. Less resin is adhered to the “Habutae” fabrics woven with the raw silk of greater size deviation than those of smaller size deviation.
2. The amount of adhered resin differs according to the type of formation or degree of density of fabrics. But in the case of the some fabric, if the number of treatment increases, so dose the adhered resin.
3. When treated with resin, a higher transmission degree of humidity is shown compared with the non-treated case.
4. The air permeability decreases as the amount of adhered resin increases.
5. The degree of water-proof improves in proportion as the adhered resin increases.
6. The ability for crease recovery increases in proportion as the amount of adhered resin increases.