チタンインプラントの生体内での遅れ破壊の機構

抄録

Fatigue tests and delayed fracture tests under sustained tensile loading of titanium were carried out. From these results, it was concluded that stress-corrosion cracking related with hydrogen was suspected for delayed fracture of small titanium devices in vivo.