6％Ni炭素鋼の摩擦攪拌接合における攪拌部の集合組織解析による流動挙動の推定

抄録

Friction stir welding (FSW) was performed under the two welding conditions (rotation speed-traveling speed) of 150 rpm-100 mm/min and 200 rpm-400 mm/min using 6 mass％Ni-0.63 mass％C steels. The slightly lower peak welding temperature and significantly higher cooling rate was obtained under the condition of 200 rpm-400 mm/min. Texture analysis for retained austenite and martensite revealed that the parent austenite had simple shear texture, which lead to the formation of {110}<111> texture in transformed martensite. Moreover, material flow behavior as a function of distance from the top surface in the stir zone was analyzed based on textures obtained by EBSD measurement. A concentric material flow, which has smaller radius as the far from the tool shoulder, was formed under the condition of 150 rpm-100 mm/min. On the other hand, a heterogeneous material flow with the center shifted to the retreating side was formed under the condition of 200 rpm-400 mm/min. In addition, a different vertical component of material flow was predicted to occur under each welding conditions.