抄録
Titanium and its alloys have various excellent properties, such as good corrosion resistance and high specific strength. However, they have not been applied to the sliding parts under sever wear condition due to their poor tribological properties.
In this study, laser alloying using graphite powder was carried out to form Ti/TiC composite surface layer on commercial pure titanium substrate for improving wear resistance. The effects of graphite powder size and laser irradiation parameters on the microstructure of laser alloyed zone were mainly investigated. In the laser alloyed zone, dendritic primary TiC and fine particles of eutectic TiC were observed. In the condition of higher laser traverse speed and larger size of graphite powder, undissolved graphite particles were observed.