訂正：Fe-P-C-Ag液体分離金属ガラスの合金設計と凝固組織

抄録

本誌第69巻第5号に掲載の永瀬丈嗣氏，寺井智之氏，松室光昭氏，武村守氏の研究論文「Fe-P-C-Ag液体分離金属ガラスの合金設計と凝固組織」につきまして，著者より訂正の申し出がありました．訂正箇所は下記の通りです．

◆P. 185 Title

（正）Alloy Design and Solidification Microstructure Analysis in Fe-P-C-Ag Immiscible Metallic Glass

（誤）Alloy Design and Solidification Microstructure Analysis of in Fe-P-C-Ag Immiscible Metallic Glass

◆P. 190 Figure caption (Fig. 8)

（正）XRD patterns of MS-ribbons of the Fe₆₀P₁₀C₁₀Ag₂₀ alloy: The upper figure corresponds to the entangled ribbons shown in Figure 7a, and the lower corresponds to the rectilinear ribbons shown in Figure 7b, respectively.

（誤）XRD patterns of MS-ribbons of the Fe₆₀P₁₀C₁₀Ag₂₀ alloy: The upper figure corresponds to the entangled ribbons shown in Figure 6a, and the lower corresponds to the rectilinear ribbons shown in Figure 6b, respectively.

◆P. 190 Figure caption (Fig. 9)

（正）TEM-BF images and selected SAED patterns of MS-ribbons of the Fe₆₀P₁₀C₁₀Ag₂₀ alloy: (a) the entangled ribbons shown in Figure 7a, and (b) the rectilinear ribbons shown in Figure 7b. TEM specimens were obtained by the double-side milling process as shown by the index (2-1) in Figure 3.

（誤）TEM-BF images and selected SAED patterns of MS-ribbons of the Fe₆₀P₁₀C₁₀Ag₂₀ alloy: (a) the entangled ribbons shown in Figure 6a, and (b) the rectilinear ribbons shown in Figure 6b. TEM specimens were obtained by the double-side milling process as shown by the index (2-1) in Figure 3.

◆P. 191 Figure caption (Fig. 10)

（正）STEM-HAADF images, Fe and Ag EDS element mapping of the rectilinear ribbons shown in Figure 7b. STEM specimens were obtained by the single-side milling process as shown by the index (2-2) in Figure 3 for the observation of WH-side in MS-ribbons.

（誤）STEM-HAADF images, Fe and Ag EDS element mapping of the rectilinear ribbons shown in Figure 6b. STEM specimens were obtained by the single-side milling process as shown by the index (2-2) in Figure 3 for the observation of WH-side in MS-ribbons.

◆P. 191 Figure caption (Fig. 11)

（正）Magnetization-magnetic field (M-H) loops of MS-ribbons of the Fe60P10C10Ag20 alloy: (a) the entangled FCC-Ag ribbons shown in Figure 7a, and (b) the Fe-P-C metallic glass rectilinear ribbons shown in Figure 7b.

（誤）Magnetization-magnetic field (M-H) loops of MS-ribbons of the Fe60P10C10Ag20 alloy: (a) the entangled FCC-Ag ribbons shown in Figure 6a, and (b) the Fe-P-C metallic glass rectilinear ribbons shown in Figure 6b.