2021 年 65 巻 4 号 p. 443-448
Purpose To evaluate the effect of different cleaning methods on the shear bond strength (SBS) of a 10-methacryloyloxydecyl dihydrogen phosphate (MDP)-containing self-adhesive resin cement to zirconia after saliva contamination.
Methods Sixty zirconia specimens were randomly divided into four groups (n=15) according to treatment surface. Except for the control group, all samples were contaminated with saliva and were then rinsed with water-spray and air-dried. Subsequently, the specimens were either treated with a cleaning paste (CP), with argon plasma (AP), or did not undergo an additional cleaning process (WS). An MDP-containing self-adhesive resin cement was applied onto the ceramic surfaces. Specimens were stored in water (24 hours) followed by thermocycling (5°C to 55°C for 10.000 cycles). SBS tests were performed in a universal testing machine, and the results (MPa ± SD) were statistically analyzed using ANOVA and Bonferroni post-hoc test. Fractured surfaces were examined to identify the failure types using a stereomicroscopy and SEM.
Results The surface cleaning treatment (p<0.05) significantly affected the results. The highest SBS values were observed in the control group (12.16 ± 1.22 MPa) and were statistically comparable to values for the CP group (11.38 ± 1.65 MPa). The AP group (9.17 ± 1.06 MPa) showed significantly higher bond strength than the WS group (6.95 ± 1.20 MPa), but it showed significantly lower strength than the control and CP groups.
Conclusions The CP application was the most effective method in removing saliva contamination. The AP treatment could not restore the SBS to the same level as uncontaminated specimens.