Effect of Different Indirect Composite Onlay and Core Materials on Fracture Resistance of Endodontically Treated Maxillary Premolars
Duangruthai ChotiwutthiphatthanaOnauma AngwaravongThidarat Angwarawong
著者情報
ジャーナル オープンアクセス 早期公開

論文ID: JPR_D_22_00049

この記事には本公開記事があります。
詳細
抄録

Purpose: To compare and evaluate the effects of different indirect composite onlay and/or core buildup materials on the fracture resistance and fracture mode of restored endodontically treated premolars.

Methods: Two conventional handmade indirect composite resins (SR Nexco (NC) and Ceramage (CM)) and two core buildup materials, dual-cure composite resin (MultiCore Flow (MC)), and short fiber-reinforced composite resin (EverX Posterior (EXP)), were selected. Sixty maxillary premolars were randomly divided into six groups (n=10). Group 1 included intact teeth (INT; negative control). Mesio-occluso-distal cavity preparation and endodontic treatment was performed on the remaining premolars. Group 2 was restored with polymer-reinforced zinc oxide eugenol intermediate restorative material (IRM; positive control), whereas the experimental groups (groups 3-6) were restored with core buildup material and indirect composite onlay (MC_NC, MC_CM, EXP_NC, and EXP_CM). The specimens received compressive loading using a universal testing machine, at 45° to the long axis with a crosshead speed of 0.5 mm/min until fracture. Fracture modes were visually analyzed. Fracture resistance was measured and statistically analyzed using two-way and one-way ANOVA (α=0.05).

Results: Only the type of indirect composite onlay affected the fracture resistance of the experimental groups (P=0.009). The MC_CM group showed the highest fracture resistance, which was significantly higher than that of the MC_NC group (P=0.031). No statistically significant differences were found between the INT group and other experimental groups(P>0.05). All groups had a greater incidence of restorable than unrestorable failures.

Conclusion: The type of indirect composite onlay affected the fracture resistance of restored endodontically treated maxillary premolars.

著者関連情報
© 2022 Japan Prosthodontic Society

This is an open-access article distributed under the terms of Creative Commons Attribution-NonCommercial License 4.0 (CC BY-NC 4.0), which allows users to distribute and copy the material in any format as long as credit is given to the Japan Prosthodontic Society. It should be noted however, that the material cannot be used for commercial purposes.