402 硬質薄膜の硬度/ヤング率比とトライボロジー特性(GS1,4,11 機械材料・材料加工,研究討論セッション)
詳細
Friction and wear characteristics of titanium compound coating and DLC were investigated from a consideration from hardness and young's modulus of coatings. Friction coefficient increasing and decreasing of specific wear rate were observed at high H/E value, where H is hardness and E is young's modulus. From these results, H/E value was considered to be a useful parameter for a selection of tribological useful coating.