化学的結合を介したグラフェン/CF繊維の作製および機械的特性評価

抄録

In this study, graphene oxide was grafted to carbon fibers using chemical bonding and Electrophoretic Deposition (EPD) to improve the properties of the fiber / resin interface. Graphene oxide grafted on the surface of fibers is expected to improve the mechanical properties of Carbon Fiber Reinforced Plastics (CFRPs) by improving the adhesion and its interlock to resin. At that time, the influence of the grafted graphene oxide on the mechanical properties was investigated. As a result, it was confirmed that the interface properties of the fiber were improved without the fiber strength decreasing by the grafting. In particular, the interface shear strength showed the highest value even under the preparation conditions where a uniform graft morphology was observed, and showed an increase of 41.5% compared to the untreated fiber. Finally, the improvement mechanism of the interface properties was examined. It was suggested that the main factor of the improvement was that graphene oxide was dispersed in resin around the fiber and the physical property of the resin is improved.