AE法による損傷したFRPAの破壊機構と損傷評価
鈴木 惠木田 外明相川 和人田城 宏幸
著者情報
ジャーナル フリー

2000 年 49 巻 3 号 p. 316-321

詳細
抄録

The fracture mechanisms and the damage rate of fatigue-damaged FRPA specimens are estimated by analyzing the AE signals detected during the tensile test. The loads Pi, Pb and Pc in change of the damage machanisms are determined by applying the AE energy gradient method to the nondamaged and the damaged specimens. It is found by AE frequency analysis at the loads that the damage mechanisms for nondamaged specimen are dominated by the fiber breaking, but the damage mechanisms at the lower ratio of N/Nf for the damaged specimens are dominated by the fiber debonding, the damaged mechanisms at the higher ratio of N/Nf are dominated by the fiber beraking and the damage modes at more higher ratio of N/Nf are changed by stress amplitude, where N is the number of cycles and Nf is the number of cycles to failure. It is also found by the relation between the ratio of load P/P(N) and the ratio of number of cycles N/Nf that the damage rate 1-Pi/Pi(N) is estimated higher than the damage rates 1-Pb/Pb(N) and 1-Pmax/Pmax(N), where P and P(N) are the loads in change of damage machanisms of the damaged and the nondamaged specimens, respectively.

著者関連情報
© 日本材料学会
前の記事 次の記事
feedback
Top