抄録
The present study was carried out to improve the corrosion resistance of pure magnesium in Hank’s Balanced Salt Solution (HBSS) through the surface modification. Three kinds of alkaline compounds, such as sodium hydrogen carbonate, sodium carbonate, and lithium hydroxide, were used for treatment. Only magnesium treated with aqueous sodium hydrogen carbonate solution gave a good corrosion resistance in HBSS solution at 25°C up to 75 days, while almost no effect in sodium carbonate and lithium hydroxide. It was likely that hydrogen carbonate ions were essential for the surface improvement of magnesium. X-ray diffraction patterns of modified magnesium showed new peaks of magnesium carbonate and others on the surface. New surface structure of needle-shaped crystals was observed by scanning electron microscopy (SEM). Both elemental mapping, and energy dispersive (EDX) techniques in SEM showed the precipitation of calcium magnesium phosphate (low crystallinity whitlockite:(Ca,Mg)3(PO4)2) on the surface of magnesium specimen. It could be concluded that surface modification with sodium hydrogen carbonate made it possible to apply metal magnesium in biomedical, dental, and other industrial usage.