Residual Stress of TiNi Shape Memory Alloy Thin Films with (111) Single-crystal Silicon Wafer
Tingbin WuBohong JiangXuan QiYushu LiuDong XuLi Wang
Author information
JOURNALS FREE ACCESS

2002 Volume 43 Issue 3 Pages 566-570

Details
Abstract

As micro-actuator materials, TiNi shape memory alloy thin films with substrate are used more and more in MEMS field. The residual stress in Ti-rich TiNi thin films with silicon substrate prepared by the magnetron-sputtering technique is measured by both X-ray glancing and contour method. The influence of crystallization annealing temperature and film thickness on the residual stress is tested. It is shown that the tensile residual stress decreases from 106 to 37 MPa with increasing annealing temperature from 723 to 923 K. However, it increases again above 1023 K. While increasing the film thickness from 2.4 to 6.5 \\micron, the residual stress reduces from 323 to 80 MPa. A lot of beautiful sunflower-like structures in crystal grains are observed by OM and TEM. The origin of the residual stress and its affecting factors are discussed. The thermal stress during cooling after annealing is the main factor resulting in tensile stress and the formation of martensite phase will release a part of tensile stress.

Information related to the author
© 2002 The Japan Institute of Metals and Materials
Previous article Next article
feedback
Top