Improvement of Corrosion Resistance of Vanadium Alloys in High-Temperature Pressurized Water
Mitsuhiro FujiwaraToshiya SakamotoManabu SatouAkira HasegawaKatsunori AbeKazuo KaiuchiTakemi Furuya
Author information
JOURNALS FREE ACCESS

2005 Volume 46 Issue 3 Pages 517-521

Details
Abstract

Corrosion tests in pressurized and vaporized water were conducted for V-based high Cr and Ti alloys and V-4Cr-4Ti type alloys containing minor elements such as Si, Al and Y. Weight losses were observed for every alloy after corrosion tests in pressurized water. It was apparent that addition of Cr effectively reduced the weight change in pressurized water. The weight loss of V-4Cr-4Ti type alloys in corrosion tests in vaporized water was also reduced as Cr content increased. The V-20Cr-4Ti alloy had a slight weight gain, almost same as that of SUS316, which had the best corrosion properties in the tested alloys. The elongation of alloys with in excess of 10% Cr was reduced as Cr content increased. The elongations of the V-12Cr-4Ti and the V-15Cr-4Ti alloys were significantly reduced by corrosion and cleavage fracture was observed reflecting hydrogen embrittlement. The reduced elongations of the alloys were recovered to the same level of as annealed conditions after hydrogen degassing. After corrosion, the V-15Cr-4Ti-0.5Y alloy still kept enough elongation, suggesting that the addition of Y is effective to reduce the hydrogen embrittlement.

Information related to the author
© 2005 The Japan Institute of Metals and Materials
Previous article Next article
feedback
Top