Influence of Casting Defects on Tensile Properties of ADC12 Aluminum Alloy Die-Castings
A. K. M. Aziz AhamedHiroshi Kato
Author information

2008 Volume 49 Issue 7 Pages 1621-1628


Cold flakes, one of casting defects, were observed through acoustic microscopy in aluminum alloy die-cast plates (ADC12), and specimens having a cold flake of different sizes were prepared and subjected to the tensile testing. The tensile strength linearly decreased with the size of the cold flake, and the decreasing rate of the strength was greater for the specimen with the exposed cold flake than that with the embedded cold flake. The in-process ultrasonic measurement was carried out during tensile testing, and it was found that the oxide layer of the cold flake was detached from the matrix to form a crack before final failure. Then by using the linear fracture mechanics, the critical value Kc* at failure was evaluated to be 8–10 MPa·m1⁄2 from the tensile strength, which value was slightly lower than the fracture toughness of the matrix of 11–14 MPa·m1⁄2.

Information related to the author
© 2008 Japan Foundary Engineering Society
Previous article Next article